Suprapto, Agus ORCID: https://orcid.org/0000-0003-4172-4163, Setyawan, Pungky Eka, Setiawan, Aries Boedi ORCID: https://orcid.org/0000-0002-1265-092X and Tsamroh, Dewi Izzatus ORCID: https://orcid.org/0000-0002-0752-6529 (2019) The Effect Of Anodizing Solution Type Against The Coating Thickness And Wear Rate Of Aluminum 6061. International Journal of Mechanical Engineering and Technology (IJMET), 10 (12). pp. 57-64. ISSN Print: 0976-6340 and ISSN Online: 0976-6359

Preview	Text THE EFFECT OF ANODIZING SOLUTION TYPE...pdf Download (706kB) | Preview
Preview	Text Hasil Cek Turnitin.pdf Download (3MB) | Preview

Abstract

Aluminum is metal that mild and has a fairly high mechanical strength. It is widely used in automotive industry, aircraft industry, but, aluminum has disadvantage which is low wear resistance. Development of methods for improving the wear rate can be conducted by using anodizing method. The study aimed to obtain accurate and detail information that needed to support the wear rate analysis results using anodizing solution of sulfuric acid and phosporic acid. The method used in this study was using
experimental testing with variations of voltage and immersion time on solution type of sulfuric acid and phosporic acid. Analysis of the test results obtained from the
thickness test, wear rate test and microstructure test by using Scanning Electron Microscopy (SEM). SEM was used to characterize the microstructure of coating on aluminium that resulted from anodizing process.SEM was conducted on specimen that had the lowest and the highest value of wear rate. According to the resultsobtained that voltage and time of anodizing affected the wear rate of aluminium 6061. The
more time and voltage of anodizing, the lower the wear rate value, thus the wear resistance of aluminium improved 14 times higher than the wear resistance of base metal.